Synthesis and characterization of lanthanum- and yttrium-doped Fe2O3 pigments

Cerâmica

D. M. A. Melo¹  M. A .f. Melo¹  A. E. Martinelli¹  Z. R. Silva¹  J. D. Cunha¹  A. C. Lima¹ 

[1] ,UFRN Department of Chemistry Natal RN

关键词: rare earths;    ceramic pigments;    colorimetry;    terras raras;    pigmentos cerâmicos;    colorimetria;   

DOI  :  10.1590/S0366-69132007000100012

来源: SciELO

【 摘 要 】

Iron oxide has been doped with rare earth ions (yttrium or lanthanum) aiming at producing ceramic pigments with hues that vary from orange to brown. The powders were synthesized from polymeric precursors using the Pechini method and subsequently calcined between 900 and 1100 ºC. The resulting pigments were characterized by BET, X ray diffraction, colorimetric analysis, UV-visible, infrared (FTIR), particle size distribution and thermal analysis. The color depicted by La/Fe powders changed as the calcination temperature increased from 900 ºC to 1100 ºC, as established by the corresponding changes in the values of the colorimetric coordinates from L* a* b* = 49.003, 10.541, 12.609 to L* a* b* = 31.279, 6.096, 6.877. On the other hand, Y/Fe powders were little affected by similar changes in the calcination temperature, revealing the effect of yttrium on the color stability of the powder. The values of the colorimetric coordinates in this case varied from L* a* b* = 45.230, 17.315, 28.750 to L* a* b* =51.631, 15.726, 25.825. Structural changes were also noticed as a function of the size of the rare earth ion added to the structure. Upon calcination at 900°C, lanthanum stabilized the ABO3-type perovskite structure whereas the presence of yttrium resulted in a mixture of oxides.

【 授权许可】

CC BY-NC   
 All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License