Elaboration of Alumina-Zirconia Composites: Role of the Zirconia Content on the Microstructure and Mechanical Properties

Materials

Valentina Naglieri¹  Paola Palmero¹  Laura Montanaro¹ 

[1] Laboratorio di Tecnologia ed Ingegnerizzazione dei Materiali Ceramici (LINCE) Lab., Department of Applied Science and Technology, INSTM R.U. PoliTO, Politecnico di Torino, Corso Duca degli Abruzzi, 24, Torino 10129, Italy; E-Mails:

关键词: Al₂O₃-ZrO₂;    nanocomposites;    microstructure;    mechanical properties;   

DOI  :  10.3390/ma6052090

来源: mdpi

【 摘 要 】

Alumina-zirconia (AZ) composites are attractive structural materials, which combine the high hardness and Young’s modulus of the alumina matrix with additional toughening effects, due to the zirconia dispersion. In this study, AZ composites containing different amounts of zirconia (in the range 5–20 vol %) were prepared by a wet chemical method, consisting on the surface coating of alumina powders by mixing them with zirconium salt aqueous solutions. After spray-drying, powders were calcined at 600 °C for 1 h. Green bodies were then prepared by two methods: uniaxial pressing of spray-dried granules and slip casting of slurries, obtained by re-dispersing the spray dried granulates. After pressureless sintering at 1500 °C for 1 h, the slip cast samples gave rise to fully dense materials, characterized by a quite homogeneous distribution of ZrO₂ grains in the alumina matrix. The microstructure, phase composition, tetragonal to monoclinic transformation behavior and mechanical properties were investigated and are here discussed as a function of the ZrO₂ content. The material containing 10 vol % ZrO₂ presented a relevant hardness and exhibited the maximum value of K_I0, mainly imputable to the t → m transformation at the crack tip.

【 授权许可】

CC BY   
© 2013 by the authors; licensee MDPI, Basel, Switzerland.