Cobalt Molybdenum Carbides: Preparation and Reactivity for Methane Decomposition

JOURNAL OF CHEMICAL ENGINEERING OF JAPAN

Hiroyuki Kanesugi¹  Masatoshi Nagai¹ 

[1] Graduate School of Bio-Applications and Systems Engineering, Tokyo University of Agriculture and Technology

关键词: Cobalt Molybdenum;    Hydrogen Production;    Methane Decomposition;    Surface Properties;   

DOI  :  10.1252/jcej.39.569

来源: Maruzen Company Ltd

【 摘 要 】

References(11)Cited-By(4)The decomposition of methane for hydrogen production over a Co–Mo catalyst with 25% Co loading carbided at various temperatures was studied at 973 K and atmospheric pressure. The 700 K-carbided catalyst was the most active of the other catalysts for H2 production (above 98%) in the decomposition at 44 h. The Co–Mo catalysts carbided at 725 and 750 K were also active at 44 h, while the catalyst carbided at 800 K was active for 1 h but quickly deactivated. The catalysts carbided at 873 and 973 K were less active. The XRD analysis showed that the catalysts carbided at 700–750 K consisted of MoO2 and CoMoO4 which were turned to CoMoOxCy, β-Mo2C, and Co metal during the CH4 decomposition. The carbiding at 800 K produced CoMoOxCy which changed to β-Mo2C and Co metal after the reaction. The carbiding at 873 and 973 K contained β-Mo2C and Co metal. The effects of two carbiding methods of different heating rates, H2 pretreatment, and CO2 addition on the catalytic activity and hydrogen production were studied.

【 授权许可】

Unknown