Examination of Corrosion Products and the Alloy Surface After Crevice Corrosion of a Ni-Cr-Mo- Alloy | |
Shan, X. ; Payer, J.H. | |
United States. Department of Energy. Yucca Mountain Project Office. | |
关键词: Chemical Composition; Crevice Corrosion; 36 Materials Science; Corrosion Products; Surface Properties; | |
DOI : 10.2172/893817 RP-ID : NA RP-ID : NA RP-ID : 893817 |
|
美国|英语 | |
来源: UNT Digital Library | |
【 摘 要 】
The objective of this study is to investigate the composition of corrosion products and the metal surface within a crevice after localized corrosion. The analysis provides insight into the propagation, stifling and arrest processes for crevice corrosion and is part of a program to analyze the evolution of localized corrosion damage over long periods of time, i.e. 10,000 years and longer. The approach is to force the initiation of crevice corrosion by applying anodic polarization to a multiple crevice assembly (MCA). Results are reported here for alloy C-22, a Ni-Cr-Mo alloy, exposed to a high temperature, concentrated chloride solution. Controlled crevice corrosion tests were performed on C-22 under highly aggressive, accelerated condition, i.e. 4M NaCl, 100 C and anodic polarization to -0.15V-SCE. The crevice contacts were by either a polymer tape (PTFE) compressed by a ceramic former or by a polymer (PTFE) crevice former. Figure 1 shows the polarization current during a crevice corrosion test. After an incubation period, several initiation-stifle-arrest events were indicated. The low current at the end of the test indicated that the metal surface had repassivated.
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
893817.pdf | 388KB | download |