Structural and magnetic properties of zinc- and aluminum-substituted cobalt ferrite prepared by co-precipitation method | |
S T Alone12  K M Jadhav1  | |
[1] Department of Physics, Dr. B. A. Marathwada University, Aurangabad 431 004, India$$;Shiv Chhatrapati College, Aurangabad 431 004, India$$ | |
关键词: Ferrite; co-precipitation; magnetization; AC susceptibility.; | |
DOI : | |
学科分类:物理(综合) | |
来源: Indian Academy of Sciences | |
【 摘 要 】
Spinal ferrites having the general formula Co1-ð‘¥Znð‘¥Fe2-ð‘¥Alð‘¥O4 (ð‘¥ = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6) were prepared using the wet chemical co-operation technique. The samples were annealed at 800°C for 12 h and were studied by means of X-ray diffraction, magnetization and low field AC susceptibility measurements. The X-ray analysis showed that all the samples had single-phase cubic spinel structure. The variation of lattice constant with Zn and Al concentration deviates from Vegard's law. The saturation magnetization ðœŽð‘ and magneton number ð‘›B measured at 300 K using high field hysteresis loop technique decreases with increasing ð‘¥, suggesting decrease in ferrimagnetic behaviour. Curie temperature ð‘‡C deduced from AC susceptibility data decreases with ð‘¥, suggesting a decrease in ferrimagnetic behaviour.
【 授权许可】
Unknown
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO201912040497508ZK.pdf | 350KB | download |