Electric properties of textured (K$_{0.44}$Na$_{0.52}$Li$_{0.04}$)(Nb$_{0.86}Ta$_{0.10}$Sb$_{0.04}$)O$_3$ thick film prepared by screen printing method

Bulletin of materials science

FANG FU¹  JIWEI ZHAI³  ZHENGKUI XU² 

[1] Luoyang Institute of Science and Technology, Luoyang 471023, China$$Luoyang Institute of Science and Technology, Luoyang 471023, ChinaLuoyang Institute of Science and Technology, Luoyang 471023, China$$;Department of Physics and Materials Science, City University of Hong Kong, Kowloon Tong, Hong Kong$$Department of Physics and Materials Science, City University of Hong Kong, Kowloon Tong, Hong KongDepartment of Physics and Materials Science, City University of Hong Kong, Kowloon Tong, Hong Kong$$;Functional Materials Research Laboratory, Tongji University, Shanghai 200092, China$$Functional Materials Research Laboratory, Tongji University, Shanghai 200092, ChinaFunctional Materials Research Laboratory, Tongji University, Shanghai 200092, China$$

关键词: Screen printing;    ferroelectricity;    piezoelectricity;    nonlinear property.;   

DOI  :  

学科分类：材料工程

来源: Indian Academy of Sciences

【 摘 要 】

Textured (K$_{0.44}$Na$_{0.52}$Li$_{0.04}$) (Nb$_{0.86}$Ta$_{0.10}$Sb$_{0.04}$)O$_3$ thick film was fabricated by the screen printing method with plate-like NaNbO3 particles as template. Thick film with 75% grain orientation was prepared. Remnant polarization and coercive field observed from the P�?�E loops of textured thick film were 3.6 $mu$C cm$^{�?2}$ and 21 kV cm$^{�?1}$, respectively. Textured (K$_{0.44}$Na$_{0.52}$Li$_{0.04}$) (Nb$_{0.86}$Ta$_{0.10}$Sb$_{0.04}$)O$_{3}$ thick film exhibited diffusion behaviour by analysing the temperature dependence of permittivity and loss tangent. The result of leakage current density showed a conduction mechanism of Schottky emission. Piezoelectric (PZT) properties of the thick film were characterized by the relationship of unipolar strain and applied electric field and the PZT constant $d^∗_{33}$ of textured thick film reached to 150 pm V$^{�?1}$. Nonlinear PZT property of the thick film was investigated by Rayleigh law.

【 授权许可】

Unknown