Effect of sintering temperature and time on the mechanical properties of Co�?�Cr�?�Mo/58S bioglass porous nano-composite | |
Majid Taghian Dehaghani1  Mehdi Ahmadian1  | |
[1] Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran$$Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, IranDepartment of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran$$ | |
关键词: Porous; compressive strength; nano-composite.; | |
DOI : | |
学科分类:材料工程 | |
来源: Indian Academy of Sciences | |
【 摘 要 】
In the present study, Co�?�Cr�?�Mo/58S bioglass porous nano-composite samples were successfully produced using 30 wt% carbonate hydrogen ammonium and polyvinyl alcohol solution as space holder and binder, respectively. The cold compacted samples were heated at 175°C for 2 h and then were heated to sinter at 1100, 1150, 1200 and 1250°C for 3, 6, 9 and 12 h. True porosity of samples was measured and the samples were characterized using the X-ray diffraction (XRD) technique, scanning electron microscopy (SEM) and compressive test. Although the results of compression test for samples sintered at 1200 and 1250°C showed that the shape of stress�?�strain curves were similar to each other, compacted powders sintered at 1100 and 1150°C exhibited some fluctuations. Moreover, the compressive strength increased by decreasing the true porosity, indicating the role of high temperature on the sintering process. In addition, volume diffusion was predominant mechanism for these samples at sintering temperature of 1250°C. SEM images of the porous sample sintered at 1250°C for 3 h showed an appropriate range of pore sizes and interconnectivity. The XRD results showed that there are no contaminations and new phase is detectable in the sintered porous samples.
【 授权许可】
Unknown
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO201912010230261ZK.pdf | 1111KB | download |