Sol Freeze Dry Nd:YAG Nanopowder Synthesis and Sinterability Studies

Defence Science Journal

Sheikh Ashfaq Ahmed¹  Khavangkhui Zimik¹  Kiranmala Laishram¹  Rekha Mann¹  Neelam Malhan¹ 

[1]Laser Materials Division, Laser Science and Technology Centre

关键词: Freeze dry;    Nd:YAG;    transparent ceramic;    vacuum sintering;    HIP;    Nd:YAG nanopowder;    sinterability;   

DOI  :  

学科分类：社会科学、人文和艺术（综合）

来源: Defence Scientific Information & Documentation Centre

【 摘 要 】

Citrate nitrate sol freeze dry synthesis of 2 atomic % neodymium ion doped Yttrium Aluminium Oxide (Nd:YAG) nanopowders was explored for the first time. Sol was prepared by dissolving nitrates of Al3+, Y3+ and Nd3+ keeping molar ratio to be 5: 2.94: 0.06. Total metal ion to citric acid ratio was optimised at 1 is to 0.25. Sol was freeze dried at -80 °C for 48 h. Dried mass thus obtained was calcined at 1000 °C for 2 h to give phase pure Nd:YAG as characterised by FTIR and XRD. Particles were in the size range of 35 nm - 50 nm with close to spherical morphology as observed by TEM. Nanopowder was compacted and sintered at 1700 °C for 5 h under 10-6 mbar followed by hot isostatic press at 1750 °C for 4 h under 200 MPa, to give 71 per cent transmission at 1064 nm indicating synthesis of well sinterable Nd:YAG nanopowders.

【 授权许可】

Unknown