Thermal Stability of Wood Fibers Produced from Recycled Medium Density Fiberboards
Ahmadi, Mohammad1  Moezzipour, Aida2  Moezzipour, Bita3 
[1] SveučiliÅ¡te Mohaghegh Ardabili, Fakultet agronomije i prirodnih resursa, Zavod za drvo, papir i tehnologiju, Ardabil, Iran;SveučiliÅ¡te u Teheranu, Fakultet prirodnih znanosti, Zavod za drvo, papir i tehnologiju, Karaj, Iran;University of Mohaghegh Ardabili, Faculty of Agriculture and Natural Resources, Wood and Paper Science and Technology Department, Ardabil, Iran
关键词: thermal stability;    recycled fibers;    MDF;    electrical heating;    hydrothermal;   
DOI  :  10.5552/drvind.2019.1833
学科分类:农业科学(综合)
来源: Sveuciliste u Zagrebu
PDF
【 摘 要 】

In this study, thermal stability of fibers obtained from recycled MDF was investigated and compared with virgin fibers by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Two different methods, including electrical heating and hydrothermal treatment, were used for recycling the MDF wastes. Electrical heating method was performed at two different times (2 and 4 min) and hydrothermal method was done at three different temperatures (105, 125 and 150 °C). Chemical structure of wood fibers was also studied. TGA and DSC analysis showed higher weight loss of recycled fibers as compared to virgin fibers in a similar degradation region, which means that thermal stability of recycled fibers is lower than virgin fibers. In fact, thermal behavior of recycled fibers was medium between wood and UF resin. DSC analysis showed two exotherms at around 340 and 475 °C. The transition at around 340 °C in fibers thermogram was considered to be due to polysaccharides thermal deterioration and the exotherm at 475 °C was related to lignin carbohydrate complex deterioration. The results of chemical structure analysis showed that lignin and hemicellulose content of recycled fibers was significantly lower than that of virgin fibers, which resulted in decreased thermal stability.

【 授权许可】

CC BY   

【 预 览 】
附件列表
Files Size Format View
RO201910250909009ZK.pdf 516KB PDF download
  文献评价指标  
  下载次数:26次 浏览次数:14次