Microstructure and Plasticity of Hot Deformed 5083 Aluminum Alloy Produced by Rapid Solidification and Hot Extrusion / Badania Mikrostruktury I Plastyczności Odkształcanego Na Gorąco Szybko-Krystalizowanego I Wyciskanego Stopu Aluminium 5083

Archives of Metallurgy and Materials

T. Tokarski¹  Ł. Wzorek¹  H. Dybiec¹ 

[1] AGH UNIVERSITY OF SCIENCE AND TECHNOLOGY, FACULTY OF NON-FERROUS METALS, 30-059 KRAKÓW, 30 MICKIEWICZA AV., POLAND

关键词: Keywords: rapid solidification;    Al-Mg alloy;    thermal stability;    superplasticity;   

DOI  :  10.2478/v10172-012-0140-2

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The objective of the present study is to analyze the mechanical properties and thermal stability for rapidly solidified and extruded 5083 aluminum alloy (RS). Compression tests were performed in order to estimate flow stress and strain rate sensitivity relation for 5083 alloy in the temperature range of 20°C to 450°C. For the comparison purposes, conventionally cast and extruded industrial material (IM) was studied as well. Deformation tests performed at room temperature conditions show that rapidly solidified material exhibits about 40% higher yield stress (YS=320 MPa) than conventionally cast material (YS=180 MPa), while the deformation at 450°C results in significant decrease of flow stress parameters for RS material (YS=20 MPa) in comparison to IM material (YS=40 MPa). Strain rate sensitivity parameter determined for high temperature conditions indicates superplasticity behavior of RS material. Structural observations show that under conditions of high-temperature deformation there are no operating recrystallization mechanisms. In general, grain size below 1µm and size of reinforcing phases below 50 nm is preserved within the used deformation temperature range.