Properties and microstructure of twin-roll cast Al-Mg alloy containing Sc and Zr

4th International Conference Recent Trends in Structural Materials

Cieslar, M.^1 ; Bajer, J.^1 ; Zimina, M.^1 ; Šlapáková, M.^1 ; Grydin, O.^2

Faculty of Mathematics and Physics, Charles University, Ke Karlovu 5, Prague 2

121 16, Czech Republic^1

Faculty of Mechanical Engineering, University Paderborn, Pohlweg 47-49, Paderborn

33098, Germany^2

关键词: Al-Mg alloy;    Annealed materials;    Fine dispersions;    Microhardness and microstructure;    Properties and microstructures;    Strengthening effect;    Temperature intervals;    Twin roll cast;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/179/1/012012/pdf
DOI  :  10.1088/1757-899X/179/1/012012

来源: IOP

【 摘 要 】

The influence of Sc and Zr on microhardness and microstructure of twin-roll cast Al-Mg alloy was studied. A significant effect of Sc and Zr on hardening of the material after annealing in a temperature interval between 250 C and 400 C was confirmed. Maximal hardness was obtained after annealing above 300 C due to a precipitation of a fine dispersion of Sc and Zr containing precipitates. An exposure of the annealed material to higher temperatures suppresses the influence of these particles due to changes of the strengthening effect of precipitates. However, a partially positive role of remaining precipitates hindering recrystallization persists even up to 550 C.