The Kinetics of Phase Transformations During Continuous Cooling of the Ti6Al4V Alloy from the Single-Phase β Range

Archives of Metallurgy and Materials

R. Dąbrowski¹ 

[1] Faculty of Metals Engineering and Industrial Computer Science Department of Physical and Powder Metallurgy, AGH University of Science and Technology, 30-059 Kraków, 30 Mickiewicza Av., Poland;

关键词: Keywords: phase transformations;    microstructure;    hardness;    dilatometric curve;    CCT diagram;   

DOI  :  10.2478/v10172-011-0077-x

学科分类：金属与冶金

来源: Akademia Gorniczo-Hutnicza im. Stanislawa Staszica / University of Mining and Metallurgy

【 摘 要 】

The paper reports on a study of the kinetics of phase transformations during continuous cooling of the alpha-beta Ti6Al4V titanium alloy from the β range. After cooling from 1020°C at a rate higher than critical the martensitic β ← α' transformation occurred. At rates lower than critical in addition to the martensitic reaction also the diffusional β ← α transformation took place. Metallographic examination of samples cooled at various rates within the range of diffusional transformations, revealed variations in the α phase morphology changing from lamellar, after cooling at between 7.3 and 0.015°C/s, to granular, as observed after cooling at 0.012°C/s. The phase transformations were also clearly seen in dilatometric curves.