Influence of different heat treatment programs on properties of sol–gel synthesized (Na0.5K0.5)NbO3 (KNN) thin films
关键词: Sol–gel;    ferroelectric;    electrical properties;    thin film;    perovskite;    lead-free.;   
学科分类:材料工程
来源: Indian Academy of Sciences
PDF
【 摘 要 】

Thin films of (Na0.5K0.5)NbO3 (KNN) were synthesized on Pt/Ti/SiO2/Si substrates with repeated spin-coating after fabrication of the precursor solution by a sol–gel process. The KNN precursor solution was prepared from K- and Na-acetate, Nb-pentaethoxide and 1,3-propanediol. Based on three characteristic temperatures derived from thermal analysis (TG–DTA) experiments, five heat treatment programs were developed. All programs lead to single phase perovskite KNN films with random crystal orientation, but only the programs that included a treatment after each single spin-coating step provided pore free surfaces with grains of about 100 nm size. The lowest leakage current at 150 kV cm-1 was obtained for the temperature program that included pyrolysis and calcination steps after each deposited layer.

【 授权许可】

CC BY   

【 预 览 】
附件列表
Files Size Format View
RO201902180115564ZK.pdf 548KB PDF download
  文献评价指标  
  下载次数:13次 浏览次数:27次