Effects of growth rate on the physical and mechanical properties of Sn-3.7Ag-0.9Zn eutectic alloy

International Journal of Physical Sciences

U. Bouml¹ 

关键词: Alloys;    crystal growth;    microstructure;    mechanical properties;    electrical properties.;   

DOI  :  10.5897/IJPS2013.3855

学科分类：物理（综合）

来源: Academic Journals

【 摘 要 】

Sn-3.7wt.%Ag-0.9wt.%Zn alloy was directionally solidified upward under different conditions, with different growth rates (V = 3.38 - 220.12 µm/s) at a constant temperature gradient (G = 4.33 K/mm) and with different temperature gradients (G = 4.33 -12.41 K/mm) at a constant growth rate (V = 11.52 µm/s) by using a Bridgman-type directional solidification furnace. The microstructure was observed to be a rod Ag3Sn structure in the matrix of β-Sn from the directionally solidified Sn-3.7wt.%Ag-0.9wt.%Zn samples. The microhardness, tensile strength and electrical resistivity of alloy were measured from directionally solidified samples. The dependency of the microhardness, tensile strength and electrical resistivity on the solidification parameters for directionally solidified Sn-Ag-Zn eutectic alloy was investigated and the relationships between them were experimentally obtained by using regression analysis. The results obtained in the present work were compared with the previous similar experimental results.

【 授权许可】

CC BY