The effect of heat treatment on mechanical properties and microstructure of additively manufactured components

5th International Conference Recent Trends in Structural Materials

Hrbáková, T.^1 ; Simson, T.^2 ; Koch, J.^2 ; Wolf, G.^3

COMTES FHT A.s., Prmyslová 995, Dobany

334 41, Czech Republic^1

Ostbayerische Technische Hochschule Amberg-Weiden, Czech Republic^2

Fraunhofer-Institut für Umwelt-, Sicherheits-und Energietechnik UMSICHT, Czech Republic^3

关键词: Ageing temperature;    Air cooling;    Effect of heat treatments;    Properties and microstructures;    Solution annealing;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/461/1/012026/pdf
DOI  :  10.1088/1757-899X/461/1/012026

来源: IOP

【 摘 要 】

Components from maraging steel MS1 (1.2709) and aluminium alloy AlSi10Mg were fabricated by additive manufacturing (AM). As-built and heat-treated components were analysed in terms of mechanical properties and microstructure. The heat treatment of the material MS1 was performed by a solution annealing at 850°C for 1 hour, ageing temperature at 480°C for 3 hours and air cooling. The heat treatment of the AlSi10Mg was performed by stress relieve at 300°C for 2 hours. Ostbayerische Technische Hochschule Amberg-Weiden carried out tensile tests of as-built and heat-treated samples. Samples were afterwards analysed in COMTES FHT a.s. for further tests of porosity and microstructure using optical and scanning electron microscopy. The aim of the present work is to show the change of mechanical properties and the microstructure with a heat treatment after AM.