Mechanical Properties Study of High Impact Polystyrene Under Impact and Static Tests

23rd International Conference on Manufacturing

Hýlová, L.^1 ; Mizera, A.^1 ; Mizera, M.^1 ; Grund, R.^2 ; Ovsík, M.^1

Tomas Bata University in Zlín, Nám. T.G. Masaryka 5555, Zlín

760 01, Czech Republic^1

TREVOS A.s., Maov 34, Trutnov

511 01, Czech Republic^2

关键词: Crosshead speed;    High impact polystyrene;    Injection moulded samples;    Static tests;    Tensile-impact test;    Three-point bending test;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/448/1/012044/pdf
DOI  :  10.1088/1757-899X/448/1/012044

来源: IOP

【 摘 要 】

This article deals with the study of high impact polystyrene (HIPS) mechanical properties. Injection moulded samples were subjected to the tensile impact test, tensile test, impact test - Charpy and three-point bending test at the ambient temperature. Tensile test was measured at two crosshead speeds 50 and 500 mm/min and bending test at 2 and 50 mm/min. The results show the great adaptability of HIPS which classify this material to the group of very well adaptable polymers to different loadings.