Microstructure and Properties of Nickel - Based Superalloy C-276 Pulse Laser Weld Joints Based on 0.381mm Thickness

2018 International Conference on Advanced Electronic Materials, Computers and Materials Engineering

材料科学;无线电电子学;计算机科学

Wang, Junchao^1 ; Xu, Desheng^1 ; Wang, Ying^1

Key Laboratory of Automobile Materials, School of Materials Science and Engineering, Jilin University, Changchun

130025, China^1

关键词: Columnar dendrites;    Equi-axed grains;    Fracture mode;    Hastelloy C-276;    Microstructure and properties;    Nickel- based superalloys;    Secondary phasis;    Sheet material;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/439/2/022020/pdf
DOI  :  10.1088/1757-899X/439/2/022020

来源: IOP

【 摘 要 】

Based on Hastelloy C-276 sheet materials, the microstructure, element segregation and mechanical properties of weld joints were studied using pulse laser welding technology. It is noted that there are three morphological grains in the weld zone, which is columnar dendrites, cellular crystals and equiaxed grains, respectively. Compared with the base metal, the microstructure of the weld zone is obviously refined. Element segregation exists in the weld zone where no secondary phases formed. In addition, the microhardness of the weld joints is greater than that of the base metal by 12%. Its yield strength is equivalent to the yield strength of the base metal, and the tensile strength is 93% of that of the base metal. There are plenty of dimples in the fracture of the weld joints and the base metal, and the fracture modes of both are all ductile fracture.