Electrospinning synthesis of Li-Fe-P/PAN based micro-nanofibers as precursors for LiFePO4 cathode material in Li-ion fiber battery applications

3rd International Congress of Mechanical Engineering and Agricultural Science

机械制造;农业科学

Cortes, M.A.^1,2,3 ; Castano, N.^1,2,3 ; Garcia, E.^1,2,3 ; Martinez, H.V.^1,2,3

Mechanical Engineering Department, Grupo de Investigación Sobre Nuevos Materiales (GINUMA), Universidad Pontificia Bolivariana, Medellín, Colombia^1

Mechanical Engineering Department, Grupo de Investigación Energía y Termodinámica (GET), Universidad Pontificia Bolivariana, Medellín, Colombia^2

Nanotechnology Engineering Department, Universidad Pontificia Bolivariana, Medellín, Colombia^3

关键词: Electrochemical performance;    Electrochemical phenomena;    Electrospinning method;    Electrospinning parameters;    Energy dispersive X ray spectroscopy;    Energy storage systems;    Micro/nano particle;    Morphological features;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/437/1/012006/pdf
DOI  :  10.1088/1757-899X/437/1/012006

学科分类：农业科学（综合）

来源: IOP

【 摘 要 】

The increase popularity of wearable devices and smart textiles are being held back partly by better energy storage systems, which are based on electrochemical phenomena. Research in novel materials with optimal morphologies for better electrochemical performance is one the paths being followed. Micro/nano fibers are interesting morphologies as they present high surface areas, less agglomeration and flexibility, compared to micro/nano particles. In this article, precursor fibers for LiFePO4 cathode material, defined as lithium-iron-phosphorous/polyacrylonitrile (Li-Fe-P/PAN) precursor nanofibers, have been synthesized by the electrospinning method. The influence of electrospinning parameters such as voltage (V), flow rate (F) and distance between the collector and the tip of the syringe needle (D), on the morphology of the fibers have been studied mainly by scanning electron microscopy (SEM). Optimal morphological features such as less formation of beads, small fiber diameter, less polydispersity and high fiber alignment, were observed at V = 14 kV, F = 0.7 mL/h and D = 14 cm. The occurrence of nanofibers on the precursor Li-Fe-P/PAN material was observed through SEM, while the energy dispersive x-ray spectroscopy (EDS) confirms the presence of the fundamental elements in the precursor nanofibers.