Effect of strain path change on the texture evolution after cold rolling and recrystallization of Nickel-40 wt. %Cobalt alloy

18th International Conference on Textures of Materials

材料科学;物理学

Shankar, Gyan^1 ; Suwas, Satyam^1

Department of Materials Engineering, Indian Institute of Science, Bangalore

560 012, India^1

关键词: Annealing twins;    Cross rolling;    Deformation texture;    Recrystallization texture;    Texture transition;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/375/1/012018/pdf
DOI  :  10.1088/1757-899X/375/1/012018

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Effect of change in strain path during rolling and its role in the development of crystallographic texture after deformation and then after recrystallization has been studied for Ni-40wt%Co which is a medium stacking fault energy (SFE) material. Results indicate that textures developed after unidirectional rolling and multi-step cross-rolling are quite different which also leads to different texture evolution after recrystallization. Microstructure of both UDR and cross rolled sample shows band type of feature within the grain having lesser band density for cross rolled samples. After recrystallization unidirectionally rolled sample shows bimodal whereas cross rolled sample shows equiaxed grain size distribution. But all the samples show large fraction of annealing twins. It has been shown that in all cases formation of annealing twins have large influence on the texture transition after recrystallization.