Texture evolution of 01570 aluminum alloy sheet | |
Chen, X.M.^1 ; Fan, Y.Y.^1 ; Pan, Q.L.^2 ; Liu, C.Y.^3 | |
School of Electronic and Information and Mechanical Engineering, Zhaoqing University, Zhaoqing | |
526061, China^1 | |
School of Materials Science and Engineering, Central South University, Changsha | |
410083, China^2 | |
School of Mechanical Engineering, Guangdong Applied Science and Technology University, Zhaoqing | |
526061, China^3 | |
关键词: Aluminum alloy sheet; Deformation texture; Evolution mechanism; Recrystallization temperatures; Recrystallization texture; Stabilizing annealing; Temperature rising; Texture components; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/170/1/012013/pdf DOI : 10.1088/1757-899X/170/1/012013 |
|
来源: IOP | |
![]() |
【 摘 要 】
The texture configuration and evolution mechanism of 01570 aluminum alloy, under different stabilizing annealing systems, were studied by means of observations of optical microscopy and analysis of X-Ray. The results show that the major textures of 01570 alloy sheet, at cold-rolling condition, are of Brass texture{011}, Copper texture {112} and S texture{123}; especially, the strength of Brass texture is strongest. Below the recrystallization temperature to make stabilizing annealing, the texture components change little compared with the cold-rolling sheet. When stabilizing annealing temperature reaches the recrystallization temperature, the deformation texture will disappear with the temperature rising gradually, and the recrystallization texture configuration will gradually increase; when the temperature reaches 590°C, the major textures are of the recrystallization texture of rotating cube texture and cube texture in the alloy.【 预 览 】