Mechanical and physical properties of selected magnesium base nanocomposites

2018 International Conference on Material Strength and Applied Mechanics

材料科学;力学

Drozd, Z.^1 ; Trojanová, Z.^1 ; Luká, P.^1 ; Kueráková, M.^2 ; Václav, T.^2

Faculty of Mathematics and Physics, Charles University, Ke Karlovu 3, Prague 2

CZ-121 16, Czech Republic^1

Department of Structure Analysis, Institute of Physics, Czech Academy of Sciences, Cukrovarnická 10, Prague 6

CZ-162 00, Czech Republic^2

关键词: Dynamic moduli;    Hot extrusion;    Linear thermal expansions;    Mechanical and physical properties;    Wide temperature ranges;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/372/1/012004/pdf
DOI  :  10.1088/1757-899X/372/1/012004

来源: IOP

【 摘 要 】

The effect of various nanoparticles (BN, Al2O3, ZrO2, Gr) on the mechanical and physical properties of magnesium was studied in the present paper. Microcrystalline magnesium reinforced with nanoparticles was prepared by ball milling and hot extrusion. Microhardness of samples was measured at room temperature. The linear thermal expansion of the nanocomposites was measured over a wide temperature range from RT up to 400°C. Dynamic modulus and amplitude dependent internal friction were measured at room temperature. Although all nanocomposites were prepared with the same technology substantial differences in mechanical and physical properties were estimated among various nanocomposites. Bonding between magnesium matrix and ceramic and graphite nanoparticles plays important role for the resulting nanocomposites properties.