Investigation on magnetic field dependent modulus of epoxidized natural rubber based magnetorheological elastomer | |
Yunus, N.A.^1 ; Mazlan, S.A.^1 ; Ubaidillah^1,2 ; Aziz, S.A.A.^1 ; Khairi, M. H. Ahmad^1 ; Wahab, N.A.A.^1 ; Shilan, S.T.^1 | |
Vehicle System Engineering Research Laboratory, Malaysia - Japan International Institute of Technology, Universiti Teknologi Malaysia, Jalan Sultan Yahya Petra, Kuala Lumpur | |
54100, Malaysia^1 | |
Mechanical Engineering Department, Faculty of Engineering, Universitas Sebelas Maret, Central Java, Jl. Ir. Sutami 36A, Kentingan, Surakarta | |
57126, Indonesia^2 | |
关键词: Carbonyl iron particles; Dynamic moduli; Dynamic shears; Epoxidized natural rubber; Excitation frequency; Exposed to; Magnetorheological elastomers; Storage and loss modulus; | |
Others : https://iopscience.iop.org/article/10.1088/1742-6596/776/1/012024/pdf DOI : 10.1088/1742-6596/776/1/012024 |
|
来源: IOP | |
【 摘 要 】
This paper presents an investigation on the use of epoxidized natural rubber (ENR) as a matrix of magnetorheological elastomers (MREs). Isotropic ENR-based MRE samples were synthesized by homogeneously mixed the ENR compound with carbonyl iron particles (CIPs). The microstructure of the sample was observed, and the magnetic field-dependent moduli were analyzed using rheometer. The influences of excitation frequency, CIPs content and magnetic field on the field-dependent moduli of ENR-based MREs were evaluated through dynamic shear test. The microstructure of MRE samples demonstrated the dispersed CIPs in the ENR matrix. The remarkable increment of storage and loss moduli of the ENR-based MREs has exhibited the magnetically controllable storage and loss moduli of the samples when exposed to the magnetic field. Consequently, the CIPs content, frequency and magnetic field were significantly influenced the dynamic moduli of the ENR-based MREs.【 预 览 】