Synthesis and Characterization Hierarchical Three-Dimensional TiO2 Structure via Hydrothermal Method

5th International Conference on Advanced Materials Sciences and Technology

Syuhada, N.^1 ; Yuliarto, B.^1 ; Nugraha^1,2

Advance Functional Materials Laboratory, Department of Engineering Physics, Fakultas Teknologi Industri, Institut Teknologi Bandung, 40132, Indonesia^1

Research Center for Nanoscience and Nanotechnology (NRCN), Institut Teknologi Bandung, Fakultas Teknologi Industri, 40132, Indonesia^2

关键词: Hexadecyltrimethylammonium bromide;    Hierarchical structures;    Hierarchically structure;    Hydrothermal process;    One-dimensional nanostructure;    Spherical morphologies;    Synthesis and characterizations;    Threedimensional (3-d);   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/367/1/012052/pdf
DOI  :  10.1088/1757-899X/367/1/012052

来源: IOP

【 摘 要 】

TiO2is one of the most potential candidates due to its fascinating properties for multi-discipline fields. One dimensional nanostructure TiO2such as nanotube and nanorods has been widely used for many devices technology. Compare with one-dimensional nanostructure TiO2; the hierarchical TiO2 has not been widely applied. Three dimensional TiO2play a promising role for application in many different fields such as photovoltaics, photocatalytic and a gas sensor. Herein, we report that the hierarchically structures TiO2have been successfully obtained by the one-pot Hydrothermal process. The growth mechanism of Titania was controlled by Titanium (IV) isopropoxide (TTIP). Ethylene glycol (EG). Hydrochloric acid (HCl). Hexadecyltrimethylammonium bromide (CTAB) molar ratio. TTIP was used as titanium source and CTAB as a soft template. The molar ratio of TTIP. EG. HCl. CTAB was 0.1:0.2:0.4:0.001. Those samples were synthesized using the hydrothermal method at 180 °C for 20 h. The purpose of this work was focused on investigating morphology, crystallite size, crystalline phase, and particle size. The properties of these materials were characterized by XRay Diffraction, Energy Dispersive Spectroscopy and Scanning Electron Microscope. It was found all particles exhibited unique spherical morphology which arranged by nanorods and good distribution nanoparticle. The Average size of the sphere has range 1 μm to 3 μm with diameter nanorods 60 nm to 100 nm. The TiO2spheres were constructed of interconnected nanorods and formed a three dimensional (3D) porous framework. XRD analysis confirmed that sample consisted of pure rutile crystal structure with crystallite size was 50 nm, and EDS revealed an elemental content of Ti 61.03 % and O 38.97 %.