Synthesis of biodegradable plastic from tapioca with N-Isopropylacrylamid and chitosan using glycerol as plasticizer

2nd International Conference on Oleo and Petrochemical Engineering

Syaubari^1 ; Safwani, S.^1 ; Riza, M.^1

Chemical Engineering Department, Engineering Faculty of Syiah, Kuala University - Darussalam, Banda Aceh, Indonesia^1

关键词: Biodegradable plastics;    Elongation values;    FT-IR spectrum;    Grafting process;    Group formations;    Poly-n-isopropyl acrylamide;    Polymer grafting;    Single bond;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/345/1/012049/pdf
DOI  :  10.1088/1757-899X/345/1/012049

来源: IOP

【 摘 要 】

One of natural polymers that can be used as raw material in the manufacture of biodegradable plastic is tapioca and chitosan. The addition of other compounds such as glycerol as plasticizer is to improve the characteristics of the plastic that already produced. N- Isopropylacrylamid (NIPAm) is an organic compound that can be synthesized into a polymer or polymer grafting which also biodegradable too. This research aims tostudy the synthesis of biodegradable plastics from tapioca with the addition of chitosan, NIPAm, poly(NIPAm) and analyze the characteristics of biodegradable plastics that already produced. This research was done in three stages, there are (1) polymerization NIPAm, (2) the grafting of chitosan-poly NIPAm and (3) the synthesis of biodegradable plastics from starch mixture with variation of addition chitosan, NIPAm, poly(NIPAm), chitosan-graft-poly(NIPAm) and also variations of glycerol as plasticizer. The results of this research is a thin sheet of plastic which is will get analyzed for the characteristics of functional groups, mechanical, morphological and its biodegradability. FTIR spectra showed the grafting process with the new group formation of CO single-bond at 850 cm-1. Plastic with the addition of NIPAm and 1 ml glycerol has the highest tensile strength value about 31.1 MPa. Plastic with poly(NIPAm) and 4 ml glycerol produces the highest elongation value about 153.72%. Plastic with Chitosan-graft-poly(NIPAm) with 1 ml glycerol has the longest biodegradation because of the small mass-loss for six weeks which is about 6.6%.