Synthesis and Characterization of Chitosan-p-t-Butylcalix[4]arene acid | |
Handayani, D.S.^1 ; Frimadasi, W.^1 ; Kusumaningsih, T.^1 ; Pranoto^1 | |
Department of Chemistry, Faculty of Mathematics and Natural Sciences, Sebelas Maret University, Indonesia^1 | |
关键词: Amorphous phase; Aromatic bonds; Diisopropylcarbodiimide; Fourier transform infra reds; FTIR analysis; Melting point temperature; Surface area analysis; Synthesis and characterizations; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/333/1/012011/pdf DOI : 10.1088/1757-899X/333/1/012011 |
|
来源: IOP | |
【 摘 要 】
The synthesis of chitosan-p-t-butylcalix[4]arene acid was done with DIC (N, N'-diisopropylcarbodiimide) as the coupling agent. The structural analysis of the chitosan-p-t-butylcalix[4]arene acid was conducted by spectrophotometer Fourier Transform Infra Red (FTIR) and X-Ray Diffraction (XRD). Meanwhile, the surface area was investigated by Surface Area Analysis, the Scanning Electrone Microscope (SEM) analysed the surface morphology, and also the melting point temperature was determined. FTIR analysis on Chitosan-p-t-butylcalix[4]arene provides an overlapped absorption of -OH and -NH groups at 3438.26 cm-1. Meanwhile, a C = C aromatic bond present at 1480.43 cm-1. XRD analysis shows some broaden peaks due to the amorphous phase of the prepared material. The prepared material is a brownish yellow solid, odorless and porous. The melting point, surface area, and the average pore radius are above 300 °C, 9.42 m2/ g, and 52.5938 Å, respectively.