Effect of pressing temperature on the mechanical properties of waste styrofoam filled sawdust composite

TALENTA - Conference on Engineering, Science and Technology 2017

工业技术;自然科学

Nasution, H.^1 ; Harahap, H.^1 ; Riani, R.^1 ; Pelawi, A.I.^1

Department of Chemical Engineering, Faculty of Engineering, Universitas Sumatera Utara, Padang Bulan, Medan

20155, Indonesia^1

关键词: Impact testers;    Instron;    Non-polar;    Pressing temperature;    Weight fractions;    Wood fiber;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/309/1/012034/pdf
DOI  :  10.1088/1757-899X/309/1/012034

来源: IOP

【 摘 要 】

This study has investigated the effect of pressing temperature on mechanical properties of waste styrofoam composite filled with sawdust. The waste styrofoam as the matrix was mixed with sawdust as filler and maleic anhydride (6%wt) as a compatibilizer. The weight fraction ratio between matrix and filler 70:30 (wt) and wood fiber size of 100 mesh were conducted. The pressing temperatures were investigated using a hot press with temperatures varied viz. 120, 130, 150, and 170 °C. Surface modification was applied to sawdust to diminish its polarity so that it could be compatible with the non-polar waste styrofoam matrix. Composites were evaluated using Instron and impact tester machine to investigate the tensile strength and impact strength of the material, respectively. The result indicated that tensile strength has decreased with the increase of pressing temperature where the largest tensile strength is at 130 °C of 33 MPa. The same trend has occurred on impact strength, where the value has reached of 300 J/cm2on pressing temperature of 130 °C. From scanning electron microscopy (SEM) analysis it is also confirmed that during impact test, the resistance of the composite which has been pressed at the temperature of 130 °C have given better morphology than the composite at 170 °C.