Field Electron Emission Characteristics of Single-Walled Carbon Nanotube on Tungsten Blunt Tip

2nd International Conference on Advanced Materials

Mousa, Marwan S.^1 ; Daradkeh, Samer^1

Surface Physics and Materials Technology Lab, Department of Physics, Mu'Tah University, Al-Karak, Jordan^1

关键词: Electron currents;    Electron emitters;    Electron field emission;    Emission characteristics;    Field electron emissions;    Fowler-Nordheim plots;    IV characteristics;    Singlewalled carbon nanotube (SWCNT);   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/305/1/012022/pdf
DOI  :  10.1088/1757-899X/305/1/012022

来源: IOP

【 摘 要 】

Recent investigations that are presented here illustrate the initial results that were obtained from a modified technique for holding the CNT on a W clean blunt tip. Field Electron Emission (FEE) has been investigated for single walled carbon nanotube (SWCNT) mounted on tungsten tip under (∼10-8mbar) vacuum conditions. The measurements recorded presented results showed that the CNT mounted on the W tip could emit electron current of at (0.7 V/μm) and reach up to (24 μA) of emission current at normal emission conditions. Such electron field emission tip was fabricated by electrolytically etching the high purity tungsten wire of (0.1 mm) in diameter in NaOH of (0.1) Molar solution, then mounting the single-walled carbon nanotube on the tip to be nearest to the tin oxide-coated and phosphorus glass anode. Such process was possible to be carried out under the microscope. A field electron microscope with a tip-screen separation at (∼10mm) was used to characterize the electron emitter. The system was evacuated to an ultra-high vacuum level obtained after initial backing the system at up to (∼180 °C) overnight. The emission characteristic has been investigated employing the I-V characteristics with Fowler-Nordheim plots and recording the emission images.