Repair welding of cast iron coated electrodes

5th ModTech International Conference - Modern Technologies in Industrial Engineering

Zuk, M.^1 ; Górka, J.^1 ; Dojka, R.^2 ; Czupryski, A.^1

Silesian University of Technology, Mechanical Engineering Faculty, Chair of Welding, Konarskiego 18a, Gliwice

44-100, Poland^1

Silesian University of Technology, Mechanical Engineering Faculty, Department of Foundry, Towarowa 7, Gliwice

44-100, Poland^2

关键词: Coated electrodes;    Complex production;    Microscopic study;    Penetration testing;    Repair welding;    Welding current;    Welding materials;    Welding process;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/227/1/012139/pdf
DOI  :  10.1088/1757-899X/227/1/012139

来源: IOP

【 摘 要 】

Welding cast iron is a complex production procedure. Repair welding was used to repair damaged or poorly made castings. This is due to a tendency to cracking of the material during welding as well as after it. Welding cast iron can be carried out on hot or on cold. Hot welding requires high heat material and the use of welding material in the form of cast iron. In the case of cold welding, it is possible to use different materials. Mostly used filler metals are nickel and copper based. The work shows the course of research concerning repairmen of ductile iron with arc welding method. For the reparation process four types of ESAB company coated electrodes dedicated for cast iron were used with diameter 3.2 and 4 mm: ES 18-8-6B (4mm), EB 150 (4mm), OK NiCl, EM. In the cast iron examined during the testing grooves were made using plasma methods, in order to simulate the removed casting flaws. Then the welding process with coated electrodes was executed. The process utilized low welding current row of 100A, so there would only be a small amount of heat delivered to the heat affected zone (HAZ). Short stitches were made, after welding it was hammered, in order to remove stresses. After the repair welding the part of studies commenced which purpose was finding surface defects using visual testing (VT) and penetration testing (PT). In the second part, a series of macro and microscopic studies were executed witch the purpose of disclosuring the structure. Then the hardness tests for welds cross sections were performed. An important aspect of welding cast iron is the colour of the padding weld after welding, more precisely the difference between the base material and padding weld, the use of different materials extra gives the extra ability to select the best variant. The research of four types of coated electrode was executed, based on the demands the best option in terms of aesthetic, strength and hardness.