Preparation of Low fouling Polyethersulfone Membranes by Simultaneously Phase Separation and Redox Polymerization

4th International Conference on Advanced Materials Science and Technology

Roihatin, A.^1 ; Susanto, H.^2

Conversion Energy Department, Polytechnic State Semarang, Jl. Prof. Soedarto-Tembalang, Semarang, Indonesia^1

Department of Chemical Engineering, Diponegoro University, Jl. Prof. Soedarto-Tembalang, Semarang, Indonesia^2

关键词: Fouling resistance;    Membrane characterization;    Morphology structures;    NIPS;    Polyethersulfone membrane;    Redox polymerization;    UF membranes;    Water permeability;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/202/1/012004/pdf
DOI  :  10.1088/1757-899X/202/1/012004

来源: IOP

【 摘 要 】

This paper presents preparation of low fouling PES membranes by non solvent induced phase separation (NIPS) coupled with redox polymerization. The membrane characterization included water permeability, morphology structure (by SEM) and surface chemistry (by FTIR). Water permeability measurements showed thatthe membranes have water permeability within the range 10-50 L/h.m2.bar. Addition of PEG dan PEGMA intopolymer solution increased water permeability, whereas blending redox initiator and crosslinker, MBAA in polymer solution decreased water permeability. Surface morfology of membranes by SEM showed that unmodified PES membrane had smaller pore size than PEG or PEGMA modified PES membranes. Furthermore, PES-PEG or PES-PEGMA membranes modified by blending with redox initiator and MBAA as crosslinker showed smaller pore size than unmodified membrane. FTIR analysis showed that all membranes have typical spectraof PES polymer; however no additional peak was observed forthe membranes prepared with addition of PEG/PEGMA, initiator redox and also crosslinker. The addition of PEG/PEGMA, redox initiator and crosslinker resulted in membranes with high rejection and an acceptable flux as well as more stable due to relatively high fouling resistance.