Forming a single layer of a composite powder based on the Ti-Nb system via selective laser melting (SLM)

International Seminar on Interdisciplinary Problems in Additive Technologies

材料科学;物理学

Saprykin, A.A.^1 ; Sharkeev, Yu.P.^2 ; Ibragimov, E.A.^1 ; Babakova, E.V.^1 ; Dudikhin, D.V.^1

Yurga Institute of Technology, TPU Affiliate, Leningradskaya str.26, Yurga, Russia^1

Institute of Strength Physics and Materials Science, Siberian Branch, Russian Academy of Sciences, 2/4, pr. Akademicheskii, Tomsk, Russia^2

关键词: Composite powders;    Implant production;    Inert properties;    Orthopedic surgery;    Powdered materials;    Process condition;    Process Variables;    Selective laser melting;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/140/1/012001/pdf
DOI  :  10.1088/1757-899X/140/1/012001

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Alloys based on the titanium-niobium system are widely used in implant production. It is conditional, first of all, on the low modulus of elasticity and bio-inert properties of an alloy. These alloys are especially important for tooth replacement and orthopedic surgery. At present alloys based on the titanium-niobium system are produced mainly using conventional metallurgical methods. The further subtractive manufacturing an end product results in a lot of wastes, increasing, therefore, its cost. The alternative of these processes is additive manufacturing. Selective laser melting is a technology, which makes it possible to synthesize products of metal powders and their blends. The point of this technology is laser melting a layer of a powdered material; then a sintered layer is coated with the next layer of powder etc. Complex products and working prototypes are made on the base of this technology. The authors of this paper address to the issue of applying selective laser melting in order to synthesize a binary alloy of a composite powder based on the titanium-niobium system. A set of 10x10 mm samples is made in various process conditions. The samples are made by an experimental selective laser synthesis machine "VARISKAF-100MB". The machine provides adjustment of the following process variables: laser emission power, scanning rate and pitch, temperature of powder pre-heating, thickness of the layer to be sprinkled, and diameter of laser spot focusing. All samples are made in the preliminary vacuumized shielding atmosphere of argon. The porosity and thickness of the sintered layer related to the laser emission power are shown at various scanning rates. It is revealed that scanning rate and laser emission power are adjustable process variables, having the greatest effect on forming the sintered layer.