6th International Conference on Nanomaterials by Severe Plastic Deformation | |
Twins in asymmetrically rolled AZ31 analyzed with a Transmission Electron Microscope Orientation mapping tool | |
材料科学;化学 | |
Rauch, E.F.^1 ; Forget, M.^1 ; Kapelski, G.^1 | |
Science et Ingénierie des Matériaux et des Precédés, Université de Grenoble/CNRS, Grenoble INP-UJF, 38402 Saint-Martin d'Hères, France^1 | |
关键词: Asymmetrical rolling; Az31 sheets; double twins; Nano scale; Orientation mapping; Orientation maps; Shear components; Structural feature; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/63/1/012150/pdf DOI : 10.1088/1757-899X/63/1/012150 |
|
学科分类:材料科学(综合) | |
来源: IOP | |
【 摘 要 】
An AZ31 sheet was rolled in symmetrical and asymmetrical conditions to a total reduction of 50%. Twins and double twins are the dominant structural features observed after deformation. They were analyzed systematically with the help of a dedicated TEM attachment that provides orientation maps at nanoscale. This particular characterization technic is similar to SEM-EBSD tools but far less sensitive to strains. Twinning is shown to differ substantially with the introduction of a shear component. Despite their frequency, it is argued that twins have little effect on the forming process.