Production of ultrafine grained aluminum by cyclic severe plastic deformation at ambient temperature

6th International Conference on Nanomaterials by Severe Plastic Deformation

材料科学;化学

Bereczki, P.^1,2 ; Szombathelyi, V.^1,2 ; Krallics, G.^2

Department of Material Science, College of Dunaújváros, Dunaújváros, Hungary^1

Department of Materials Science and Engineering, Budapest University of Technology and Economics, Budapest, Hungary^2

关键词: Flow curves;    MaxStrain System;    Microhardness measurement;    Monotonic deformation;    Multiaxial forging;    Plane strain compression tests;    Principle of virtual velocities;    Severe plastic deformations;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/63/1/012140/pdf
DOI  :  10.1088/1757-899X/63/1/012140

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

In the present study the possibilities of grain refinement was investigated by applying large-scale of cyclic plastic deformation to aluminum at ambient temperature. The specimens are processed by multiaxial forging, which is one of the severe plastic deformation techniques. The aim of the experiments with the aluminum alloy 6082M was the determination of the equivalent stress and strain by multiaxial forging and the investigation of evolution of mechanical properties in relation with the accumulated deformation in the specimen. The mechanical properties of raw material was determined by plane strain compression test as well as by hardness measurements. The forming experiments were carried out on Gleeble 3800 physical simulator with MaxStrain System. The mechanical properties of the forged specimens were investigated by micro hardness measurements and tensile tests. A mechanical model, based on the principle of virtual velocities was developed to calculate the flow curves using the measured dimensional changes of the specimen and the measured force. With respect to the evolution of these curves, the cyclic growth of the flow stress can be observed at every characteristic points of the calculated flow curves. In accordance with this tendency, the evolution of the hardness along the middle cross section of the deformed volume has also a nonmonotonous characteristic and the magnitudes of these values are much smaller than by the specimen after plane strain compression test. This difference between the flow stresses respect to the monotonic and non-monotonic deformation can be also observed. The formed microstructure, after a 10-passes multiaxial forging process, consists of mainly equiaxial grains in the submicron grain scale.