Fabrication and Characterization of Fe doped TiO2 particles by combination the sol-gel and hydrothermal processes

2nd International Conference on Competitive Materials and Technological Processes

Bae, D.S.^1,2

School of Nano and Advanced Materials Engineering, Changwon National University, Gyeongnam, 641-773, Korea, Republic of^1

Korea Science Academy, 899 Danggam 3-dong, Busanjin-gu, Busan, Korea, Republic of^2

关键词: Fabrication and characterizations;    High temperature and pressure;    Hydrothermal process;    Reaction temperature;    Synthesized particles;    Temperature conditions;    Temperature range;    TiO2 nano-particles;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/47/1/012029/pdf
DOI  :  10.1088/1757-899X/47/1/012029

来源: IOP

【 摘 要 】

Iron doped TiO2nanoparticles were prepared under the high temperature and pressure conditions by mixture of metal nitrates solution and TiO2sol. Fe doped TiO2particles were reaction at the temperature range of 170°C-200°C for 6 h. The microstructure and phase of synthesized particles were studied by SEM(FE-SEM), TEM and XRD. Thermal properties of the synthesized particles were investigated by TG-DTA analysis. Also, Specific Surface Area of synthesized particles were studied by BET analysis. X-ray diffraction pattern shows that the synthesized particles shows the coexistence of anatase and rutile reaction at the temperature range of 170°C to 200°C for 6 h. The amount of rutile phase on the synthesized particles increased with decreasing Ag concentration in solution because the less a content of the transposition metal, the easier to phase transition in the same temperature condition. The average size and distribution of the synthesized particles was about 10nm and narrow, respectively. The average size of the synthesized particles increased as reaction temperature increased. Also, BET surface areas of synthesized particles by a hydrothermal process were found to be larger than that of pure TiO2which is synthesized by a sol-gel process.