Dielectric, electric and thermal properties of carboxylic functionalized multiwalled carbon nanotubes impregnated polydimethylsiloxane nanocomposite

6th Vacuum and Surface Sciences Conference of Asia and Australia

Sagar, Sadia^1 ; Iqbal, Nadeem^1 ; Maqsood, Asghari^1

Thermal Transport Lab (TTL), School of Chemical and Materials Engineering (SCME), National University of Sciences and Technology (NUST), H-12, Islamabad, Pakistan^1

关键词: Crystallization temperature;    Dielectric parameters;    Differential scanning calorimeters;    Electronic materials;    Energy dispersive X ray spectroscopy;    Functionalized multi-walled carbon nanotubes;    Melting transitions;    Polydimethylsiloxane PDMS;   

Others  :  https://iopscience.iop.org/article/10.1088/1742-6596/439/1/012024/pdf
DOI  :  10.1088/1742-6596/439/1/012024

来源: IOP

【 摘 要 】

The dielectric, electric and thermal properties of carboxylic functionalized multiwalled carbon nanotubes (F-MWCNT) incorporated into the polydimethylsiloxane (PDMS) were evaluated to determine their potential in the field of electronic materials. Carboxylic functionalization of the pristine multi walled carbon tubes (Ps-MWCNT) was confirmed through Fourier transform infrared spectroscopy, X-ray diffraction patterns for both Ps-MWCNTs and F-MWCNTs elaborated that crystalline behavior did not change with carboxylic moieties. Thermogravimetric and differential thermal analyses were performed to elucidate the thermal stability with increasing weight % addition of F-MWCNTs in the polymer matrix. Crystallization/glass transition / melting temperatures were evaluated using differential scanning calorimeter and it was observed that glass transition and crystallization temperatures were diminished while temperatures of first and second melting transitions were progressed with increasing F-MWCNT concentration in the PDMS matrix. Scanning electron microscopy and energy dispersive x-ray spectroscopy were carried out to confirm the morphology, functionalization, and uniform dispersion of F-MWCNTs in the polymer matrix. Electrical resistivity at temperature range (100-300°C), dielectric loss (tanδ) and dielectric parameters (Ε/Ε//) were measured in the frequency range (1MHz-3GHz). The measured data simulate that the aforementioned properties were influenced by increasing filler contents in the polymer matrix because of the high polarization of conductive F-MWCNTs at the reinforcement/polymer interface.