Effort of utilizing foundry sand waste and paper sludge as raw materials replacement for red brand without burning process

International Conference on Science and Technology for Environmental Protection

生态环境科学

Wati, S.E.D.F.S.^1 ; Putranto, T.W.C.^1 ; Citrasari, N.^1

Environmental Science and Technology Study Program, Biology Department, Faculty of Science and Technology, Universitas Airlangga, Surabaya, Indonesia^1

关键词: Brick quality;    Burning process;    Class-S;    Leaching process;    Paper sludge;    Pseudo-density;    Test method;    X-ray fluorescence methods;   

Others  :  https://iopscience.iop.org/article/10.1088/1755-1315/259/1/012015/pdf
DOI  :  10.1088/1755-1315/259/1/012015

学科分类：环境科学（综合）

来源: IOP

【 摘 要 】

This research's goal is to know the content of SiO2 and Al2O3 in the foundry sand, to know the selected variation as material for red brick without burning process based on SNI 15-2094-2000 on concrete red brick for walls and SNI 15-2094-1991 on the quality and the test method for concrete red brick and to know the content of heavy metal Zn from leaching process of the selected variations. The content of SiO2 and Al2O3 were tested by using X-Ray Fluorescence method, while the content of Zn at leached was tested by using Atomic Abrsoption Spectophotometry. The non-burning brick quality test was conducted in 5 stages, which are external display test, size and tolerance test, compressive strength test, harmful salt test, pseudo-density test and water absorption test. Variations of materials used are foundry sand: paper sludge: compactor ingredient in percentage is Variation A 75%:15%:10%; B 65%:25%:10%; C 55%:35%:10%; D 45%:45%:10%; E 0%:90%:10%; F 90%:0%:10%; and the Control Variation is G 90% sand:10%. The content of SiO2 and Al2O3 in the foundry sand are respectively 66.90% and 12.78%. The content of Zn in paper sludge is 54 mg/kg. The results of red brick testing shows that the selected variations are variations A, B, F which classified to Brick classs 50. Content of Zn in red brick leaching process of the selected variations are variations A, B, and F are respectively 0.61; 0.89; 0.21 mg/L.