Study of corrosion process of 38CrMoAl in flue gas

2018 6th International Conference on Mechanical Engineering, Materials Science and Civil Engineering

材料科学;机械制造;土木建筑工程

Jiang, Zhuohang^1 ; Wang, Shuzhong^1 ; Yang, Jianqiao^1 ; Wang, Dong^1 ; Cui, Chengchao^1 ; Zhang, Baoquan^1 ; Li, Jianna^1

Key Laboratory of Thermo-Fluid Science and Engineering of MOE, School of Energy and Power Engineering, Xi'An Jiaotong University, Xi'an

710049, China^1

关键词: Corrosion process;    Cyclic process;    Diffraction spectra;    Measurement methods;    Oxidation film;    Scanning electrons;    Temperature and pressures;    X-ray energies;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/542/1/012084/pdf
DOI  :  10.1088/1757-899X/542/1/012084

来源: IOP

【 摘 要 】

The experiments were carried out on 38CrMoAl at 3MPa and 150°C, which the temperature and pressure conditions were set to simulate the actual production conditions. The measurement methods included scanning electron microscopy analysis, X-ray energy diffraction spectrum analysis. The experimental results show that the corrosion of 38CrMoAl in the flue gas have a certain periodicity, and the corrosion process can be summarized as a cyclic process: oxidation-film formation-rupture-continuing oxidation. It can be inferred that as the exposure time increases, the corrosion process continues to circulate, and the cracking of the oxide film under the action of various stresses may even cause it to fall off, which would result in serious damage to the material.