The influence of chitosan concentration on morphology and conductivity of lithium aluminium titanate phosphate for solid electrolytes of lithium-ion battery application

13th Joint Conference on Chemistry

Wibowo, Arie^1 ; Indrawan, Radian Febi^1 ; Wulan Asri, Lia Amelia Tresna^1 ; Rahardi, Susanto Sigit^2 ; Purwasasmita, Bambang Sunendar^3

Department of Materials Engineering, Faculty of Mechanicals and Aerospace Engineering, ITB, Indonesia^1

Metal Industry Development Center (B4T), Indonesian Ministry of Industry, Indonesia^2

Department of Engineering Physics, Faculty of Industrial Technology, ITB, Indonesia^3

关键词: Aluminium titanate;    Chitosan concentration;    Energy storage technologies;    High energy densities;    Impedance spectroscopy;    Liquid electrolytes;    Optimum conditions;    porous LATP;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/509/1/012021/pdf
DOI  :  10.1088/1757-899X/509/1/012021

来源: IOP

【 摘 要 】

Nowadays, Lithium-Ion Battery (LIB) is considered as one of the most popular energy storage technologies due to their superior properties such as light-weight and high energy density. However, LIB technologies still lack of safety problem because utilization of liquid electrolytes may drive to explosion at high temperature. Thus, development of solid electrolytes based on lithium aluminium titanate phosphate (LATP) have attracted a lot of attention because they are safer than liquid electrolytes. However, utilization of LATP as solid electrolytes in LIB still limited because of their conductivity is lower than liquid electrolytes. Porous LATP are expected to solve this low conductivity problem by increasing their surface area and their ability to deliver ion. In this research, porous LATP were synthesized using sol gel method and chitosan as template. Concentration of chitosan were varied from 0.0-2.0% w/v to know the influence of chitosan to morphology and properties of obtained LATP. Based on X-ray Diffraction (XRD), all of samples contained LiTi2(PO4)3 (JCPDS PDF 35-0754) and AlPO4 (JCPDS PDF 11-0500), which are part of LATP. Based on Brunauer-Ernett-Teller (BET), Scanning Electron Microscope (SEM), and Electron Impedance Spectroscopy (EIS) analysis, 0.5% w/v chitosan concentration is the optimum condition to obtain the highest surface area (10.7 m2/g) and ionic conductivity (2.2×10-7 S/cm).