Effect of temperature on corrosion behaviour of N80 steel in CO2-saturated formation water

2nd International Workshop on Materials Science and Mechanical Engineering

机械制造;材料科学

Ye, Z.R.^1 ; Qiu, Z.C.^1 ; Yi, R.^1 ; Sui, P.F.^2 ; Lin, X.Q.^2 ; Li, K.^2

PetroChina Research Institute of Petroleum Exploration and Development, Beijing

100083, China^1

School of Mechanical and Electronic Engineering, China University of Petroleum, Qingdao

266580, China^2

关键词: Corrosion behaviour;    Corrosion products;    Effect of temperature;    Electrochemical test;    General corrosion rate;    Polarization curves;    Surface characterization;    Weight loss measurements;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/504/1/012040/pdf
DOI  :  10.1088/1757-899X/504/1/012040

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

Corrosion behaviour of N80 steel in CO2-saturated format ion water was studied by weight loss measurement, electrochemical test and surface characterization. The results showed that the general corrosion rate init ially increased and decreased with the increase of temperature and it reached maximum at 60 C about 10 mm/y. The polarization curves showed the similar results on corrosion rate of N80 steel after the exposure experiment in CO2-saturated format ion water. Localized corrosion was observed at the temperature of 40 C and 50 C. The XRD pattern indicated that the corrosion product was mainly composed by Fe3C when the temperature under 50C, then FeCO3 appeared when the temperature was above 50 C. At 70 C, the corrosion product was comprised of FeCO3 totally. Generally, the temperature of 60 C was the turning point for corrosion type and corrosion product transformation in the test conditions.