Synthesis and characterization of Ni nanoparticles supported on nitrogen-doped mesoporous carbon | |
Pamungkas, A.Z.^1 ; Abdullah, I.^1 ; Krisnandi, Y.K.^1 | |
Department of Chemistry, Faculty of Mathematics and Natural Sciences (FMIPA), Universitas Indonesia, Depok | |
16424, Indonesia^1 | |
关键词: Band intensity ratio; Graphite-like structures; Mesoporous carbon; N-doped; Ni Nanoparticles; Nitrogen-doped mesoporous carbons; Soft-templating; Synthesis and characterizations; | |
Others : https://iopscience.iop.org/article/10.1088/1757-899X/496/1/012003/pdf DOI : 10.1088/1757-899X/496/1/012003 |
|
来源: IOP | |
【 摘 要 】
Nitrogen-doped mesoporous carbon (N-MC) was synthesized by the soft-templating method using phloroglucinol/formaldehyde and melamine as carbon and nitrogen precursors, respectively, and Pluronic F127 as a template for the generation of mesopores inside the carbon structure. Scanning electron microscopy analysis revealed that the material had a rough surface, while Raman analysis indicated the existence of sp2-hybridized carbon rather than sp3, similar to graphite. The increase of the D-band to G-band intensity ratio indicated that N-MC has a more graphite-like structure than pristine mesoporous carbon. X-ray photoelectron spectroscopy analysis confirmed that nitrogen was successfully doped into the carbon framework. The material was then used as a support for Ni nanoparticles (Ni-NPs). The presence of Ni metal in Ni-NP@N-MC was confirmed by X-ray diffraction analysis.