Development and fabrication of PAMAM-based composite membrane module with a gutter layer of Chitosan/PAA polymer double network for CO2 separation

3rd International Conference on New Material and Chemical Industry

材料科学;化学工业

Duan, S.H.^1 ; Kai, T.^1 ; Kazama, S.^2

Research Institute of Innovative Technology for the Earth (RITE), 9-2 Kizugawadai, Kizugawa-shi, Kyoto

619-0292, Japan^1

Technical Development Bureau, Nippon Steel Corporation, 2-6-1 Marunouchi, Chiyoda-ku, Tokyo

100-8071, Japan^2

关键词: CO2 separation;    Coating solution;    Gutter layer;    Mixed gas;    PAMAM dendrimer;    Polyamidoamine dendrimers;   

Others  :  https://iopscience.iop.org/article/10.1088/1757-899X/479/1/012106/pdf
DOI  :  10.1088/1757-899X/479/1/012106

学科分类：材料科学（综合）

来源: IOP

【 摘 要 】

To improve the CO2 separation performance of a poly(amidoamine) (PAMAM) dendrimer composite membrane, a gutter layer of chitosan(CTS)/polyacrylic acid(PAA) polymer double network (DN) and its fabrication are proposed. In our previous studies, PAMAM-based composite membrane module with a gutter layer of cross-linked CTS showed high CO2 separation properties from CO2/N2 mixed gases. In this study, CTS/PAA polymer DN was used to prepare the gutter layer instead of CTS to enhance CO2 permeance and pressure durability of PAMAM-based composite membrane. A PAMAM dendrimer composite membrane module with a gutter layer of CTS/PAA polymer DN, which was prepared with a coating solution of CTS/PAA (CTS/PAA=1/2 molar ratio), showed a high permeance of 8.8 × 10-11 m3 (STP) m-2 s-1 Pa-1 with a high CO2 separation factor of 104 at 40 °C, pressure 550 kPa with a feed gas mixture CO2/N2=5/95 (vol./vol.).