Novel electrocatalytic membrane for ammonia synthesis

Ammonia--Synthesis;Electrocatalysis;Slip casting;Oxide ceramics;Fuel cells

Klinsrisuk, Sujitra ; Irvine, John T. S. ; Irvine, John T. S.

University:University of St Andrews

Department:Chemistry (School of)

关键词: Ammonia--Synthesis;    Electrocatalysis;    Slip casting;    Oxide ceramics;    Fuel cells;   

Others  :  https://research-repository.st-andrews.ac.uk/bitstream/handle/10023/1294/Sujitra%20Klinsrisuk%20PhD%20thesis.PDF?sequence=6&isAllowed=y

来源: DR-NTU

【 摘 要 】

Novel ceramic membrane cells of BaCe₀.₅Zr₀.₃Y₀.₁₆Zn₀.₀₄O[subscript(3-δ)] (BCZYZ), a proton-conducting oxide, have been developed for electrocatalytic ammonia synthesis. Unlike the industrial Haber-Bosch process, in this work an attempt to synthesise ammonia at atmospheric pressure has been made. The membrane cell fabricated by tape casting and solution impregnation comprises of a 200 μm-thick BCZYZ electrolyte and impregnated electrode composites. Electrocatalysts for anode and cathode were investigated. For the anode, the co-impregnation of Ni and CeO₂ provided excellent electrode performance including high catalytic activity, sintering stability and compatibility with the BCZYZ electrolyte. The best composition was the mixture of 25 wt% NiO and 10 wt% CeO₂. A symmetrical cell prepared with this electrode composition revealed low polarisation resistances of 1.0 and 0.45 Ωcm² in humidified 5% H₂/Ar at 400 and 500 °C, respectively. For the cathode, 25 wt% of impregnated Fe oxide provided a satisfactory performance in non-humidified N₂ atmosphere. Significant amounts of ammonia were produced from the single cell with Ni-CeO₂ anode and Fe oxide cathode at 400-500 °C under atmospheric pressure. Ammonia formation rate was enhanced by Pd catalyst addition and electrochemical performance was improved by Ru addition. The highest ammonia formation rate of 4 x 10⁻⁹ mols⁻¹cm⁻² was attained using the cell with a Pd-modified Fe cathode at 450 °C. The formation reaction of ammonia typically consumed around 1-2.5 % of total applied current while most of the applied current was employed in H⁺ reduction. The total current efficiency of around 90-100 % could be obtained from the membrane cells.