Unitized Stiffened Composite Textile Panels: Manufacturing, Characterization, Experiments, and Analysis

composite structures;carbon fiber reinforced polymer;multiscaling;unitized structures;textiles;postbuckling;Aerospace Engineering;Engineering;Aerospace Engineering

Kosztowny, CyrusSchultz, Marc R ;

University of Michigan

关键词: composite structures;    carbon fiber reinforced polymer;    multiscaling;    unitized structures;    textiles;    postbuckling;    Aerospace Engineering;    Engineering;    Aerospace Engineering;   

Others  :  https://deepblue.lib.umich.edu/bitstream/handle/2027.42/136947/ckosztow_1.pdf?sequence=1&isAllowed=y

瑞士|英语

来源: The Illinois Digital Environment for Access to Learning and Scholarship

【 摘 要 】

Use of carbon fiber textiles in complex manufacturing methods creates new implementations of structural components by increasing performance, lowering manufacturing costs, and making composites overall more attractive across industry. Advantages of textile composites include high area output, ease of handling during the manufacturing process, lower production costs per material used resulting from automation, and provide post-manufacturing assembly mainstreaming because significantly more complex geometries such as stiffened shell structures can be manufactured with fewer pieces. One significant challenge with using stiffened composite structures is stiffener separation under compression. Axial compression loading conditions have frequently observed catastrophic structural failure due to stiffeners separating from the shell skin. Characterizing stiffener separation behavior is often costly computationally and experimentally.The objectives of this research are to demonstrate unitized stiffened textile composite panels can be manufactured to produce quality test specimens, that existing characterization techniques applied to state-of-the-art high-performance composites provide valuable information in modeling such structures, that the unitized structure concept successfully removes stiffener separation as a primary structural failure mode, and that modeling textile material failure modes are sufficient to accurately capture postbuckling and final failure responses of the stiffened structures. The stiffened panels in this study have taken the integrally stiffened concept to an extent such that the stiffeners and skin are manufactured at the same time, as one single piece, and from the same composite textile layers. Stiffener separation is shown to be removed as a primary structural failure mode for unitized stiffened composite textile panels loaded under axial compression well into the postbuckling regime. Instead of stiffener separation, a material damaging and failure model effectively captures local post-peak material response via incorporating a mesoscale model using a multiscaling framework with a smeared crack element-based failure model in the macroscale stiffened panel. Material damage behavior is characterized by simple experimental tests and incorporated into the post-peak stiffness degradation law in the smeared crack implementation. Computational modeling results are in overall excellent agreement compared to the experimental responses.