In-Situ Fracture Studies and Modeling of the Toughening Mechanism Present in Wrought LCAC, TZM and ODS Molybdenum Flat Products.

Cockeram, B. V. ; Chan, K. S.

Technical Information Center Oak Ridge Tennessee

关键词: Molybdenum alloys;    Fracture properties;    Crack propagation;    Ductibility;    Grain boundaries;   

RP-ID  :  DE2008923317

学科分类：工程和技术（综合）

美国|英语

来源: National Technical Reports Library

【 摘 要 】

In-situ testing, ultrasonic C-scans, and metallography were used to show that a crack-divider delamination form of thin-sheet toughening occurs in wrought Low Carbon Arc Cast (LCAC) unalloyed molybdenum, Oxide Dispersion Strengthened (ODS) molybdenum, and TZM molybdenum at temperatures (ge) the Ductile to Brittle Transition Temperature (DBTT). Cracking along boundaries relieves mechanical constraint to free ligaments that may plastically stretch to produce toughening. Anisotropy in fracture toughness with lower values in the short-transverse direction is shown to produce the crack divider delaminations at the crack tip in the LT and TL orientations. The delamination zone increases with increasing stress-intensity to sizes significantly larger than the plastic zone, which leads to large increases in fracture toughness by the thin sheet toughening mechanism. Fracture in ODS Mo-alloys proceeds mainly along grain boundaries to produce small ligaments that exhibit ductility for both LT and TL orientations resulting in a lower DBTT and higher toughness values at lower temperatures than observed in LCAC and TZM. A combination of grain boundary fracture and cleavage is prevalent in LCAC molybdenum and TZM.