Phase I Single Cell Electrolyzer Test Results.

Steimke, J. ; Steeper, T.

Technical Information Center Oak Ridge Tennessee

关键词: Hydrogen;    Automotive fuels;    Electrolytes;    Ambient temperature;    Anodes;   

RP-ID  :  DE2008936320

学科分类：工程和技术（综合）

美国|英语

来源: National Technical Reports Library

【 摘 要 】

This document reports the results of Phase I Single Cell testing of an SO(sub 2)-Depolarized Water Electrolyzer. Testing was performed primarily during the first quarter of FY 2008 at the Savannah River National Laboratory (SRNL) using an electrolyzer cell designed and built at SRNL. Other facility hardware were also designed and built at SRNL. This test further advances this technology for which work began at SRNL in 2005. This research is valuable in achieving the ultimate goal of an economical hydrogen production process based on the Hybrid Sulfur (HyS) Cycle. The focus of this work was to conduct single cell electrolyzer tests to further develop the technology of SO(sub 2)-depolarized electrolysis as part of the HyS Cycle. The HyS Cycle is a hybrid thermochemical cycle that may be used in conjunction with advanced nuclear reactors or centralized solar receivers to produce hydrogen by water-splitting. Like all other sulfur-based cycles, HyS utilizes the high temperature thermal decomposition of sulfuric acid to produce oxygen and regenerate sulfur dioxide. The unique aspect of HyS is the generation of hydrogen in a water electrolyzer that is operated under conditions where dissolved sulfur dioxide depolarizes the anodic reaction, resulting in substantial voltage reduction. Low cell voltage is essential for both thermodynamic efficiency and hydrogen cost. Sulfur dioxide is oxidized at the anode, producing sulfuric acid that is sent to the high temperature acid decomposition portion of the cycle. The electrolyzer cell uses the membrane electrode assembly (MEA) concept. The anode and cathode are formed by spraying platinum containing catalyst on both sides of a Proton Exchange Membrane (PEM). In most testing the material of the PEM was NafionR. The electrolyzer cell active area can be as large as 54.8 cm(sup 2). Feed to the anode of the electrolyzer is a sulfuric acid solution containing sulfur dioxide. The partial pressure of sulfur dioxide could be varied in the range of 1 to 6 atm (15 to 90 psia). Temperatures could be controlled in the range from ambient to 80 C. Hydrogen generated at the cathode of the cell was collected for the purpose of flow measurement and composition analysis. The test facility proved to be easy to operate, versatile, and reliable.