Samples of zirconate pyrochlore ceramic (REE)2(Zr,U)2O7 (REE = La-Gd) containing simulated REE-An fraction of HLW were synthesized by two routes: (1) conventional cold compaction of oxide mixtures in pellets under pressure of 200 MPa and sintering of the pellets at 1550 C for 24 hours; and (2) using preliminary mechanical activation of oxide powders in a linear inductive rotator (LIV-0.5E) and a planetary mill - activator with hydrostatic yokes (AGO-2U) for 5 or 10 min. All the samples sintered at 1550 C were monolithic and dense with high mechanical integrity. As follows from X-ray diffraction (XRD) data, the ceramic sample produced without mechanical activation is composed of pyrochlore as major phase but contains also minor unreacted oxides. The samples prepared from pre-activated mixtures are composed of the pyrochlore structure phase only. Scanning electron microscopy (SEM) data also show higher structural and compositional homogeneity of the samples prepared from mechanically activated batches. The samples produced from oxide mixtures mechanically activated in the LIV for 10 min were slightly contaminated with iron resulting in formation of minor perovskite structure phase not detected by XRD but seen on SEM-images of the samples. Comparison of the samples prepared from non-activated and activated batches showed higher density, lower open porosity, water uptake, and elemental leaching for the samples fabricated from mechanically activated oxide mixtures.
PDF
download
878987797
028-85220240