Oak Ridge National Laboratory has developed a new technique to monitor the growth of cracks in structural members, and to predict when failure due to this damage is imminent. This technique requires the measurement of global loadings and local deflections/strains at critical locations to indicate the increasing growth of hidden cracks with sufficient warning time prior to failure to take preventative action to correct the problem or retire the structure before failure. The techniques, as described in the referenced report have been proven on a laboratory scale to successfully detect the onset of failure due to fatigue cracking (including cracking of corroded samples), stress corrosion cracking, and low temperature creep crack growth, with a reasonable degree of warning before failure.