The purpose of this work was to study the effect of exposure to humid air on the durability of a molybdenum disulfide dry film lubricant applied to spur test gears and subsequently tested in vacuum environment. This study was motivated by the James Webb Space Telescope (JWST) Mission. Some moving mechanical assembles of the JWST have been exposed to humid air during storage as a subassembly and after integration into a higher-level assembly. molybdenum disulfide dry film lubricant was applied to steel spur test gears and subsequently tested in vacuum environment. One-half of the gears had essentially zero time exposure to humid air prior to testing, and the other half were exposed to humid air of 57 percent relative humidity for exposure durations up to 77 days prior to testing. All tests were completed at the same constant torque and speed. On average, the film durability, as measured by the number of pinion revolutions, was shorter for gears exposed to humid air compared to those with zero exposure. For the unexposed gears, the durability ranged from 53,300 to 190,300 pinion revolutions with an average value of 100,200 and a median value of 83,500 revolutions. For the exposed gears, the durability ranged from 21,000 to 84,700 pinion revolutions with an average value of 64,900 and a median value of 68,800 revolutions. Using the unexposed gears as a baseline, the exposure reduced the average durability by 35 percent and the median value of durability by 18 percent. Red-brown coloration was noted on some of the gear teeth that had been exposed to humid air. The colored regions appeared as soon as 17 days after exposure to humid air. SEM inspections showed that at least some of these colored areas included material raised above the surrounding molybdenum disulfide film.
PDF
download
878987797
028-85220240