Evaluation of Cavitation-Erosion Resistance of 316LN Stainless Steel in Mercury Containing Metallic Solutes

Pawel, Steven J ; Mansur, Louis K

Oak Ridge National Laboratory

关键词: Solutes;    36 Materials Science;    Stainless Steels;    Mercury;    Shape;   

DOI  :  10.2172/931951
RP-ID  :  ORNL/TM-2006/539
RP-ID  :  DE-AC05-00OR22725
RP-ID  :  931951

美国|英语

来源: UNT Digital Library

【 摘 要 】

Room temperature cavitation tests of vacuum annealed type 316LN stainless steel were performed in pure Hg and in Hg with various amounts of metallic solute to evaluate potential mitigation of erosion/wastage. Tests were performed using an ultrasonic vibratory horn with specimens attached at the tip. All of the solutes examined, which included 5 wt% In, 10 wt% In, 4.4 wt% Cd, 2 wt% Ga, and a mixture that included 1 wt% each of Pb, Sn, and Zn, were found to increase cavitation-erosion as measured by increased weight loss and/or surface profile development compared to exposures for the same conditions in pure Hg. Qualitatively, each solute appeared to increase the post-test wetting tenacity of the Hg solutions and render the Hg mixture susceptible to manipulation of droplet shape.