Environmentally Benign Stab Detonators

Gash, A

Lawrence Livermore National Laboratory

关键词: Aluminium;    Compression;    Alloys;    Ignition;    Mixtures;   

DOI  :  10.2172/928167
RP-ID  :  UCRL-TR-217875
RP-ID  :  W-7405-ENG-48
RP-ID  :  928167

美国|英语

来源: UNT Digital Library

【 摘 要 】

Many energetic systems can be activated via mechanical means. Percussion primers in small caliber ammunition and stab detonators used in medium caliber ammunition are just two examples. Current medium caliber (20-60mm) munitions are detonated through the use of impact sensitive stab detonators. Stab detonators are very sensitive and must be small, as to meet weight and size limitations. A mix of energetic powders, sensitive to mechanical stimulus, is typically used to ignite such devices. Stab detonators are mechanically activated by forcing a firing pin through the closure disc of the device and into the stab initiating mix. Rapid heating caused by mechanically driven compression and friction of the mixture results in its ignition. The rapid decomposition of these materials generates a pressure/temperature pulse that is sufficient to initiate a transfer charge, which has enough output energy to detonate the main charge. This general type of ignition mix is used in a large variety of primers, igniters, and detonators.[1] Common primer mixes, such as NOL-130, are made up of lead styphnate (basic) 40%, lead azide (dextrinated) 20%, barium nitrate 20%, antimony sulfide 15%, and tetrazene 5%.[1] These materials pose acute and chronic toxicity hazards during mixing of the composition and later in the item life cycle after the item has been field functioned. There is an established need to replace these mixes on toxicity, health, and environmental hazard grounds. This effort attempts to demonstrate that environmentally acceptable energetic solgel coated flash metal multilayer nanocomposites can be used to replace current impact initiated devices (IIDs), which have hazardous and toxic components. Successful completion of this project will result in IIDs that include innocuous compounds, have sufficient output energy for initiation, meet current military specifications, are small, cost competitive, and perform as well as or better than current devices. We expect flash metal multilayer and sol-gel to be generic technologies applicable to a wide range of devices, especially in small caliber ammunition and sub-munitions. We will replace the NOL-130 mixture with a nanocomposite that consists of a mechanically robust energetic multilayer foil that has been coated with a sol-gel energetic material. The exothermic reactions are activated in this nanocomposite are the transformation of the multilayer material to its respective intermetallic alloy and the thermite reaction, which is characterized by very high temperatures, a small pressure pulse, and hot particle ejection. The proposed materials and their reaction products consist of, but are not limited to aluminum, nickel, iron, aluminum oxide, titanium, iron oxide and boron. These materials have much more desirable environmental and health characteristics than the NOL-130 composition.