Accelerated aging of solid lubricants for the W76-1 TSL : effects of polymer outgassing.

Dugger, Michael Thomas ; Wallace, William O. ; Huffman, Elizabeth M.

Sandia National Laboratories

关键词: Solid Lubricants;    Aging;    Lubrication And Lubricants.;    Binders;    Lubricants;   

DOI  :  10.2172/892760
RP-ID  :  SAND2006-5419
RP-ID  :  AC04-94AL85000
RP-ID  :  892760

美国|英语

来源: UNT Digital Library

【 摘 要 】

The behavior of MoS{sub 2} lubricants intended for the W76-1 TSL was evaluated after 17 and 82 thermal cycles, each lasting seven days and including a low temperature of -35 C and a high temperature of 93 C, in a sealed container containing organic materials. The MoS{sub 2} was applied by tumbling with MoS{sub 2} powder and steel pins (harperized), or by spraying with a resin binder (AS Mix). Surface composition measurements indicated an uptake of carbon and silicon on the lubricant surfaces after aging. Oxidation of the MoS{sub 2} on harperized coupons, where enough MoS{sub 2} was present at the surface to result in significant Mo and S concentrations, was found to be minimal for the thermal cycles in an atmosphere of primarily nitrogen. Bare steel surfaces showed a reduction in friction for exposed coupons compared to control coupons stored in nitrogen, at least for the initial cycles of sliding until the adsorbed contaminants were worn away. Lubricated surfaces showed no more than a ten percent increase in steady-state friction coefficient after exposure. Initial coefficient of friction was up to 250 percent higher than steady-state for AS Mix films on H950 coupons after 82 thermal cycles. However, the friction coefficient exhibited by lubricated coupons was never greater than 0.25, and more often less than 0.15, even after the accelerated aging exposures.